BPA/Bisphenol a in Dental Materials
Autor/es: HU, Hua-Jung
Director/es: Díaz-Flores García, Víctor
Titulación: Grado en Odontología
Fecha de defensa: 2021-06
Tipo de contenido:
TFG
Resumen:
Objective: Through search, the literature and understanding the release of bisphenol-A
(BPA) during treatment with the dental material, Further, would like to discuss whether it is
possible to manage it to a greater extent to promote patient safety.
Methodology: By searching information in PubMed, Google scholar, and the library of
Universidad Europea de Madrid, with a limit placed over the last 10 years, in English, and
Spanish.
Keywords: bisphenol a, dentistry, dental restoration materials, orthodontics, endodontics
and patient safety.
Results: A total of 16 studies were using. In saliva, the BPA release is increased the initial 5
min to I hour, with dental material placement show in most studies. Then BPA decreases
after 24 hours of dental material placement. In urine, BPA release was detected 24 hours
after placement. Ultimately, after 30 days, BPA will return to the level prior to placement of
the dental material. In Blood before and after treatment in adults, no BPA has been detected
in the blood serum.
Conclusion: 1. According to these studies, Bisphenol-A will release: After dental material
(orthodontic adhesive; composite resin; endodontic cement) placement in 30 min. Greater
light-curing tip distances. Show up of the oxygen inhibited layer of composite. The number
of the composite surface to be placed is positively correlated with BPA release. 2. As
dentists, protect patients' safety as far as possible without affecting dental treatment.
Certain measures can be taken to reduce the release of BPA in the clinical setting, for
example, use of rubber dams, immediate polishing of all resins used to avoid uncured layer
formulation and rinsing of the mouth after handling. Also, a preventive measure is to use a
minimum number of restorers or sealants in each appointment.